Gongtao company can make various crucibles and saggers made of high alumina, with different shapes. And we can also custom based on the requirement.
Series:
Alumina ceramic crucible
Corundum ceramic crucible
Arc alumina crucibles(high form alumina crucibles)
Cylindrical alumina ceramic crucibles
Rectangular crucibles
Special shaped crucibles
Alumina saggers
Specification: 5ml 10ml 15ml 20ml 25ml 30ml 50ml 100ml 150ml 200ml-2500ml
Points:
High alumina purity: Al2O3>99%, good corrosion resistance.
High temperature resistance, 1600C in long use, 1800C in short use.
Good thermal shock, no easy to crack.
High slip casting density
Purpose:
Main purpose of crucible and sagger is as a container for analysis and firing of material and product applied in various industries. For example: Analysis of coal, melting of the metal, analysis and firing of chemical raw materials, analysis and melting of glass, analysis and firing of rare earth materials and mineral, firing of high
Temperature items such as ceramic products and melting of single-crystal raw materials.
Useage
Under normal circumstances, firstly put the items which need to be analyzed and fired into the crucible or sagger. Then heat. The speed of heating and drop in temperature are according to the characteristics of equipment and products, fast or slow. Because of the thermal expansion of raw material which the crucibles and saggers are made of, too quick heating or cooling will easily lead to cracking of the crucibles and saggers. The best way is slowing down, which can prolong the life of them.
Series:
Alumina ceramic crucible
Corundum ceramic crucible
Arc alumina crucibles(high form alumina crucibles)
Cylindrical alumina ceramic crucibles
Rectangular crucibles
Special shaped crucibles
Alumina saggers
Specification: 5ml 10ml 15ml 20ml 25ml 30ml 50ml 100ml 150ml 200ml-2500ml
Points:
High alumina purity: Al2O3>99%, good corrosion resistance.
High temperature resistance, 1600C in long use, 1800C in short use.
Good thermal shock, no easy to crack.
High slip casting density
Purpose:
Main purpose of crucible and sagger is as a container for analysis and firing of material and product applied in various industries. For example: Analysis of coal, melting of the metal, analysis and firing of chemical raw materials, analysis and melting of glass, analysis and firing of rare earth materials and mineral, firing of high
Temperature items such as ceramic products and melting of single-crystal raw materials.
Useage
Under normal circumstances, firstly put the items which need to be analyzed and fired into the crucible or sagger. Then heat. The speed of heating and drop in temperature are according to the characteristics of equipment and products, fast or slow. Because of the thermal expansion of raw material which the crucibles and saggers are made of, too quick heating or cooling will easily lead to cracking of the crucibles and saggers. The best way is slowing down, which can prolong the life of them.
| ITEM NO. | SPECIFICATION m/m | WEIGHT KG | CAPACITY | |||
| OD ON TOP | OD AT BOTTOM | HEIGHT | THICKNESS | C.C | ||
| 2001 | 25 | 15 | 28 | 1.3 | 0.01 | 5 |
| 2002 | 29 | 18 | 34 | 1.5 | 0.02 | 10 |
| 2003 | 32 | 23 | 33 | 1.5 | 0.025 | 15 |
| 2004 | 36 | 23 | 41 | 1.7 | 0.03 | 20 |
| 2005 | 36 | 25 | 42 | 1.7 | 0.035 | 25 |
| 2006 | 38 | 25 | 45 | 1.7 | 0.04 | 30 |
| 2007 | 45 | 30 | 46 | 2 | 0.045 | 40 |
| 2008 | 48 | 30 | 52 | 2 | 0.05 | 50 |
| 2009 | 58 | 33 | 66 | 2 | 0.09 | 70 |
| 2010 | 58 | 35 | 68 | 2 | 0.10 | 100 |
| 2011 | 67 | 42 | 78 | 2.5 | 0.15 | 150 |
| 2012 | 73 | 44 | 86 | 2.5 | 0.18 | 200 |
| 2013 | 79 | 46 | 96 | 2.5 | 0.22 | 250 |
| 2014 | 83 | 50 | 106 | 2.5 | 0.25 | 300 |
| 2015 | 91 | 56 | 108 | 2.5 | 0.30 | 400 |
| 2016 | 100 | 60 | 118 | 3 | 0.40 | 500 |
| 2017 | 112 | 70 | 132 | 3 | 0.50 | 750 |
| 2018 | 125 | 80 | 146 | 3.5 | 0.70 | 1000 |
| 2019 | 140 | 90 | 170 | 4 | 1.10 | 1500 |
| 2020 | 150 | 93 | 200 | 4 | 1.40 | 2000 |
| 2021 | 160 | 100 | 200 | 4 | 1.6 | 2500 |
| 2022 | 178 | 111 | 205 | 4.5 | 2.0 | 3000 |
| Item | ||
| Chemical component | Al2O3 | ≥99 |
| R2O | ≤0.2 | |
| Fe2O3 | ≤0.1 | |
| SiO2 | ≤0.2 | |
| Vol.density(g/cm 2 ) | ≥3.80 | |
| Apparent Porosity(%) | <1 | |
| Bending Strength(Mpa) | >350 | |
| Compression strength (Mpa) | >12000 | |
| Permittivity ∑(1MHz) | 2 | |
| The max.operating temperature | 1800 | |